Alloy and Alloy wir
Cobalt-Chromium Alloys
QUEST PURE COBALT MEDIUM
Fluidity is good, and it has moderate elongation and strength.
【Composition】
Cobalt: 60.7%, Chromium: 31.0%,
Molybdenum: 6.1%, Other 2.2%
【Physical Description】
Hardness：400（HV）
Tensile Strength：785（MPa）
Elongation：7（%）
Melting Point：1388（℃）
■Metal Base, Clasp and Bar
●Specification
1㎏（Shot）
1㎏（Ingot 10g piece）
Cobalt-Chromium Alloys For Dental Casting
DAN COBALT SUPER
Blow hole is hardly generated, it excels in fluidity.
The shot can be used by a gas and oxygen dissolution.
【Composition】
Cobalt: 58%, Chromium:30%, Molybdenum:6% and Other:6%
【Physical Description】
Hardness(HV):350, Tensile Strength(MPa)735.5, Elongation(%) 13 and Melting point(℃)1400
■Metal Base, Clasp and Bar
●Form：Shot, Ingot(5, 20g piece)
●Specification：Shot 500g
1000g
Ingot(5, 20g piece) 500g
1000g
Cobalt-Chromium Alloys For Dental Casting
DAN COBALT SUPER MEDIUM
It has the moderate elongation and the strength which is similar to Super Hard.
【Composition】
Cobalt: 58.5%, Chromium:29%, Molybdenum:6% and Other:6.5%
【Physical Description】
Hardness(HV):400, Tensile Strength(MPa)760, Elongation(%) 9 and Melting point(℃)1,390
■Metal Base, Clasp and Bar
●Form：Shot, Ingot(5, 8, 20g piece)
●Specification：Shot 500g
1000g
Ingot(5, 8, 20g piece) 500g
1000g
Cobalt-Chromium Alloys For Dental Casting
DAN COBALT SUPER HARD
Compared to other Dan Cobalt series of cobalt-chromium alloys, it excels in fluidity.
Generation of blow hole is also suppressed.
The shot can be used by a gas and oxygen dissolution.
【Composition】
Cobalt: 60%, Chromium:30%, Molybdenum:6% and Other:4%
【Physical Description】
Hardness(HV):450, Tensile Strength(MPa)784.5, Elongation(%) 8 and Melting point(℃)1,388
■Metal Base, Clasp and Bar
●Form：Shot, Ingot(5, 10, 15, 20, 25, 30, 35g piece)
●Specification：Shot 500g
1000g
Ingot(5, 10, 15, 20, 25, 30, 35g piece) 500g
1000g
Cobalt-Chromium Alloys For Dental Casting
DAN COBALT
Hardness and tensile strength are heightened without reducing elongation (viscosity).
The shot can be used by a gas and oxygen dissolution.
【Composition】
Cobalt: 60.7%, Chromium:31.2%, Molybdenum:6% and Other:2.1%
【Physical Description】
Hardness(HV):450, Tensile Strength(MPa)833.6, Elongation(%) 7 and Melting point(℃)1381
■Metal Base, Clasp and Bar
●Form：shot, ingot (10, 20, 25, 30g piece)
●Specification：Shot 500g
1000g
Ingot(10, 20, 25, 30g piece) 500g
1000g
Cobalt-Chromium Alloys For Dental Casting
CONSALLIUM SUPER CAST
It is the softest in the cobalt-chromium alloys of NIHON SHIKA KINZOKU Co., Ltd. And, there is a strong stickiness.
Blow hole is hardly generated and fluidity is also good.
【Composition】
Cobalt: 54.7%, Chromium: 28%, Nickel:9%, Molybdenum: 6% and Other:2.3%
【Physical Description】
Hardness(HV):300, Tensile Strength(MPa)755.1, Elongation(%) 15 and Melting point(℃)1,400
■Metal Base, Clasp and Bar
●Form：10g piece ingot
●Specification：Ingot(10g piece) 500g
1000g
Nickel And Chromium Alloys For Dental Casting
DAN CROM SOFT Ⅲ
It excels in castability, machinability and abradability, and there is no fear of discoloration.
Please use a phosphate series investment.
【Composition】
Nickel:80.5%, Copper:7% and Chromium:6%
【Physical Description】
Hardness(HV):200, Tensile Strength(MPa) 490, Elongation(%) 10 and Melting point(℃)1,304
■Crown and Bridge
●Form：Shot
●Specification：Shot 500g
1000g
Cobalt Alloys For Metal Ceramic
DAN COBALT BOND
Because it is cobalt chrome alloys, specific gravity is light, the weight saving of technical material can be realized,
and it is high intensity, the deformatioin in burning operation is little generated.
【Composition】
Cobalt: 60.0%, Chromium: 24.0%, Molybdenum: 7.1%,
Tungsten: 5.0%, Other: 3.9%
【Physical Description】
Hardness：340（HV）(After burning）
Tensile Strength：440（MPa）
Elongation：14.8（%）
Thermal Expansion：14
Melting Point ：1355～1405（℃）
■For Metal Ceramic Of Porcelain, etc.,
●Specification
Ingot（5g piece）
100g
500g
1㎏
Brazing Filler Metal
Dan Chrome Solder
It is effective for pre-soldering of the Dan Cobalt Bond.
【Composition】
Cobalt: 60.0%, Chromium: 28.0%,
Molybdenum: 5.0%,
Silicon: 3.7%, Other: 3.3%
【Physical Description】
Melting Point：1180（℃）
■Brazing
Specification/Price
5g（8 pieces）
Alloys For Metal Ceramic (Semi Precious)
DAN BRIGHT TYPE II
It excels in property of elevated temperature and has sufficient welding reinforcement with porcelain.
【Composition】
Gold: 54.2%, Palladium: 31.0%, Silver: 4.8%, Indium 9.0%, Other 1.0%
【Physical Description】
Hardness ： 260（HV）（After burning）
Thermal Expansion： 14.1
Melting Point ： 1235（℃）
■Metal Ceramic of Porcelain, etc.,
●Specification
10g
Ingot（1g piece)
Alloys For Metal Ceramic (Semi Precious Metal)
REABLE
Taking advantage of the characteristic of semi precious, affinity with porcelain is good.
【Composition】
Gold: 40.0%, Palladium: 38.0%, Silver: 15.0%, Tin: 6.2%
Other 0.8%(Iridium, Gallium)
【Physical Description】
Hardness ： 245（HV）（After burning）
Tensile Strength ： 570（MPa）
Elongation ： 12（%）
Thermal Expansion： 14.5
Melting Point ： 1300（℃）
■Metal Ceramic of Porcelain, etc.,
●Specification
Ingot (1g piece)
Cobalt-Chromium Alloys Wire For Clasp
COBALT-CHROMIUM WIRE
It is clasp wire of cobalt-chromium alloys which has outstanding elasticity and corrosion resistance.
■Cobalt-Chromium Alloys Wire for Clasp
●Form/Specification：sphere/5m roll
●Size/Packaging/Box：0.8(φmm)/box
0.9(φmm)/box
1.0(φmm)/box
Stainless Steel Wire For Clasp (18-8 STEEL)
CLASP WIRE
It is specialized 18-8 steel wire and has outstanding elasticity and corrosion resistance as a clasp, and the falls of the elasticity by heating are few.
■Stainless Steel Wire For Clasp
●Form/Specification：Sphere/5m roll
●Size/Roll：0.8(φmm)/roll
0.9(φmm)/roll
1.0(φmm)/roll
1.1(φmm)/roll
Stainless Steel Wire For Reinforcement(18-8 STEEL)
HALF ROUND WIRE
It is for denture reinforcement. It has outstanding elasticity and corrosion resistance.
■Steel Wire for deformation and breakage prevention of denture
●Form/Specification：Half Round/3m roll
●Type/Size/Roll：Regular 1.4(width mm)/roll
1.6(width mm)/roll
1.8(width mm)/roll
2.0(width mm)/roll
Soft 1.4(width mm)/roll
1.6(width mm)/roll
1.8(width mm)/roll
2.0(width mm)/roll
Stainless Steel Wire For Reinforcement
PURE KAKYOUSHIN
It is twist wire for denture base reinforcement. It maintains firmly within a denture base and prevents breakage of denture base.
■For Deformation And Breakage Prevention of denture
●Form/Specification
Twist Wire/31cm x 3 pieces
●Size Large, Medium, Small
Stainless Steel Wire For Bar(18-8 STEEL)
LINGUAL BAR
It is for mandibular bar. It has outstanding elasticity and corrosion resistance.
Line profile is an ideal mould and it is very little tongue tactile feeling.
■Bar Wire for mandibular denture
●Form and Size are as shown on the table in the right.
●Size/Length/Packaging：Small/31cm x 3 pieces/bag
Medium/31cm x 3 pieces/bag
Large/31cm x 3 pieces/bag
Stainless Steel Wire For Bar(18-8 STEEL)
PALATAL BAR
It is for maxillary bar. It has outstanding elasticity and corrosion resistance.
Line profile is an ideal mould and it is very little tongue tactile feeling.
■Bar wire for maxillary denture
●Form and Size are as shown on the table in the right.
●Size/Length/Packaging：Small/31cm x 3pieces/bag
Medium/31cm x 3 pieces/bag
Large/31cm x 3 pieces/bag
Silver Alloys TYPE 1
QUEST PURESILVER I
Liquidus is low, it excels in operability.
【Composition】
Silver 65%, Zinc18%, Tin17%
【Physical Description】
Hardness：185（HV）
Liquidus：605 (℃)
■Inlay, Cast Core
●Packaging：100g/bag
Silver Alloys TYPE 2
QUEST PURESILVER Ⅱ
Palladium is added, so excellent corrosion resistance is realized.,
【Composition】
Silver 70%, Indium 24%, Zinc 5.6%
Other 0.4% (Palladium, Iridium)
【Physical Description】
Hardness：140（HV）
Liquidus：700 (℃)
■Inlay, Crown, Cast Core
●Packaging：100g/bag
Cobalt-Chromium Alloys
ANCHOR COBALT
It has moderate elasticity and strength.
It excels in corrosion resistance, and also economical price is set up.
【Composition】
Cobalt: 63.1%, Chromium: 28.33%,
Molybdenum: 6.01% and Other:2.35%
【Physical Description】
Hardness : 400 (HV)
Tensile Strength : 840 (Mpa)
Elongation 7 (%)
Melting Point: 1,380 (℃)
■Metal Base, Clasp and Bar
●Specification
1kg(6g piece)
Cobalt-Chromium Alloys
QUEST PURE COBALT SOFT
Hardness is low and polishing work is easy.
It is suitable for a gas and oxygen dissolution.
【Composition】
Cobalt: 60.7%, Chromium: 31.0%,
Molybdenum: 6.5% and Other:1.8%
【Physical Description】
Hardness：350（HV）
Tensile Strength：917（MPa）
Elongation：8（%）
Melting Point：1390（℃）
●Specification
1㎏（Shot）
1㎏（Ingot 10g piece）